Current PMT Prepreg Resin Systems


*All PMT resin systems are compatible with any standard reinforcements - Terms & Conditions

Resin Designation Description Work Life (days) Standard Cure Temperature (F) Frozen Shelf life
PMT-F1 Low Temp cure toughened epoxy designed for long out time and good mechanical performance 60 days 180F for  4 hrs 1 year
PMT-F2 Low Temp cure very highly toughened film adhesive 60 days 180F for  4 hrs 1 year
PMT-F3 Nano-silica loaded resin with very high modulus and very good fatigue resistance 90 days 250F for 2 hrs 1 year
PMT-F4 Toughed epoxy system with excellent mechanical properties.  90 days 250F for 2 hrs 1 year
PMT-F4-AF Highly toughened 250F curing adhesive film 90 days 250F for 2 hrs 1 year
PMT-F5-140 140F curing tooling resin that generates a Tg over 400F after post cure 3 days 140F for 10 hrs 90 days
PMT-F5TD-140 Toughened version of PMT-F5-140 designed for low temp part fabrication 3 days 140F for 10 hrs 90 days
PMT-F6-LT Toughened 250F curing cyanate ester 14 days 250F for 3 hrs 1 year
PMT-F6 Toughened 350F curing cyanate ester with a Tg of over 550F  90 days 350F for 3 hrs 1 year
PMT-F6E  High Temperature Cyanate ester  30 days 350F for 2 hrs 1 year
PMT-F7 Toughened  OOA epoxy with very good mechanical properties and High Tg 30 days 350F for 2 hrs 1 year
PMT-F14 Highly flame resistant prepreg 240 days 250F for 3 hrs 1 year
PMT-F15 Optically clear epoxy system 240 days 250 for 3 hrs 1 year
PMT-F17  Zero Particulate space grade epoxy for CNT adhesion 30 days 350F for 3 hrs 1 year
PMT-F22 High modulus epoxy prepreg for sporting goods 90 days 250F for 2 hrs 1 year
PMT-F24 Snap curing epoxy, class A surface finish 60 days 300F for 3 min 1 year
PMT-F26 High Tg, High performance rapid cure epoxy for aerospace applications 3 days 310F for 13 min 90 days
PMT-F27 Very low moisture uptake cyanate ester 30 days 350F for 3 hrs 1 year
PMT-F28 Low water uptake epoxy for space applications 30 days 350F for 3 hrs 1 year
PMT-F30 Nano-silica loaded resin with very high modulus and very good fatigue resistance 90 days 250F for 2 hrs 1 year
PMT-F31 Toughned Benzoxazine resin for High Tg and low water uptake 1 year 380F for 4 hrs 2 years